AWS ERNiCrCoMo-1 vs. S20161 Stainless Steel

AWS ERNiCrCoMo-1 belongs to the nickel alloys classification, while S20161 stainless steel belongs to the iron alloys. They have a modest 24% of their average alloy composition in common, which, by itself, doesn't mean much. There are 24 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrCoMo-1 and the bottom bar is S20161 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 28
46
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 81
76
Tensile Strength: Ultimate (UTS), MPa 710
980

Thermal Properties

Latent Heat of Fusion, J/g 330
330
Melting Completion (Liquidus), °C 1420
1380
Melting Onset (Solidus), °C 1370
1330
Specific Heat Capacity, J/kg-K 450
490
Thermal Conductivity, W/m-K 13
15
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 75
12
Density, g/cm3 8.5
7.5
Embodied Carbon, kg CO2/kg material 10
2.7
Embodied Energy, MJ/kg 140
39
Embodied Water, L/kg 350
130

Common Calculations

Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 23
26
Strength to Weight: Axial, points 23
36
Strength to Weight: Bending, points 21
29
Thermal Diffusivity, mm2/s 3.5
4.0
Thermal Shock Resistance, points 19
22

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0.8 to 1.5
0
Carbon (C), % 0.050 to 0.15
0 to 0.15
Chromium (Cr), % 20 to 24
15 to 18
Cobalt (Co), % 10 to 15
0
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 0 to 3.0
65.6 to 73.9
Manganese (Mn), % 0 to 1.0
4.0 to 6.0
Molybdenum (Mo), % 8.0 to 10
0
Nickel (Ni), % 42.7 to 61.2
4.0 to 6.0
Nitrogen (N), % 0
0.080 to 0.2
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 1.0
3.0 to 4.0
Sulfur (S), % 0 to 0.015
0 to 0.040
Titanium (Ti), % 0 to 0.6
0
Residuals, % 0 to 0.5
0