AWS ERNiCrCoMo-1 vs. S35000 Stainless Steel

AWS ERNiCrCoMo-1 belongs to the nickel alloys classification, while S35000 stainless steel belongs to the iron alloys. They have a modest 26% of their average alloy composition in common, which, by itself, doesn't mean much. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrCoMo-1 and the bottom bar is S35000 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 28
2.3 to 14
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 81
78
Tensile Strength: Ultimate (UTS), MPa 710
1300 to 1570

Thermal Properties

Latent Heat of Fusion, J/g 330
280
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1370
1410
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 13
16
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 75
14
Density, g/cm3 8.5
7.8
Embodied Carbon, kg CO2/kg material 10
3.2
Embodied Energy, MJ/kg 140
44
Embodied Water, L/kg 350
130

Common Calculations

Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 23
46 to 56
Strength to Weight: Bending, points 21
34 to 38
Thermal Diffusivity, mm2/s 3.5
4.4
Thermal Shock Resistance, points 19
42 to 51

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0.8 to 1.5
0
Carbon (C), % 0.050 to 0.15
0.070 to 0.11
Chromium (Cr), % 20 to 24
16 to 17
Cobalt (Co), % 10 to 15
0
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 0 to 3.0
72.7 to 76.9
Manganese (Mn), % 0 to 1.0
0.5 to 1.3
Molybdenum (Mo), % 8.0 to 10
2.5 to 3.2
Nickel (Ni), % 42.7 to 61.2
4.0 to 5.0
Nitrogen (N), % 0
0.070 to 0.13
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.030
Titanium (Ti), % 0 to 0.6
0
Residuals, % 0 to 0.5
0