AWS ERNiCrFe-6 vs. EN 1.3518 Steel

AWS ERNiCrFe-6 belongs to the nickel alloys classification, while EN 1.3518 steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrFe-6 and the bottom bar is EN 1.3518 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
72
Tensile Strength: Ultimate (UTS), MPa 630
630

Thermal Properties

Latent Heat of Fusion, J/g 310
260
Melting Completion (Liquidus), °C 1370
1440
Melting Onset (Solidus), °C 1320
1400
Specific Heat Capacity, J/kg-K 460
480
Thermal Conductivity, W/m-K 13
43
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 55
2.4
Density, g/cm3 8.4
7.8
Embodied Carbon, kg CO2/kg material 9.8
1.5
Embodied Energy, MJ/kg 140
20
Embodied Water, L/kg 260
51

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 21
23
Strength to Weight: Bending, points 19
21
Thermal Diffusivity, mm2/s 3.3
12
Thermal Shock Resistance, points 19
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0 to 0.080
0.93 to 1.1
Chromium (Cr), % 14 to 17
0.9 to 1.2
Copper (Cu), % 0 to 0.5
0 to 0.3
Iron (Fe), % 0 to 8.0
96.3 to 97.8
Manganese (Mn), % 2.0 to 2.7
0.9 to 1.2
Molybdenum (Mo), % 0
0 to 0.1
Nickel (Ni), % 67 to 81.5
0
Oxygen (O), % 0
0 to 0.0015
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 0.35
0.45 to 0.75
Sulfur (S), % 0 to 0.015
0 to 0.030
Titanium (Ti), % 2.5 to 3.5
0
Residuals, % 0 to 0.5
0