AWS ERNiCrFe-6 vs. EN 1.3559 Steel

AWS ERNiCrFe-6 belongs to the nickel alloys classification, while EN 1.3559 steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrFe-6 and the bottom bar is EN 1.3559 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Tensile Strength: Ultimate (UTS), MPa 630
500 to 1420

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Melting Completion (Liquidus), °C 1370
1460
Melting Onset (Solidus), °C 1320
1420
Specific Heat Capacity, J/kg-K 460
470
Thermal Conductivity, W/m-K 13
45
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 55
2.2
Density, g/cm3 8.4
7.8
Embodied Carbon, kg CO2/kg material 9.8
1.4
Embodied Energy, MJ/kg 140
19
Embodied Water, L/kg 260
50

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 21
18 to 50
Strength to Weight: Bending, points 19
18 to 36
Thermal Diffusivity, mm2/s 3.3
12
Thermal Shock Resistance, points 19
15 to 42

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0 to 0.080
0.17 to 0.23
Chromium (Cr), % 14 to 17
0.6 to 1.0
Copper (Cu), % 0 to 0.5
0 to 0.3
Iron (Fe), % 0 to 8.0
97.2 to 98.8
Manganese (Mn), % 2.0 to 2.7
0.6 to 1.0
Nickel (Ni), % 67 to 81.5
0
Oxygen (O), % 0
0 to 0.0020
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 0.35
0 to 0.4
Sulfur (S), % 0 to 0.015
0 to 0.030
Titanium (Ti), % 2.5 to 3.5
0
Residuals, % 0 to 0.5
0