AWS ERNiCrFe-6 vs. EN 1.4762 Stainless Steel

AWS ERNiCrFe-6 belongs to the nickel alloys classification, while EN 1.4762 stainless steel belongs to the iron alloys. They have a modest 20% of their average alloy composition in common, which, by itself, doesn't mean much. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrFe-6 and the bottom bar is EN 1.4762 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 34
13
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 74
78
Tensile Strength: Ultimate (UTS), MPa 630
620

Thermal Properties

Latent Heat of Fusion, J/g 310
300
Melting Completion (Liquidus), °C 1370
1410
Melting Onset (Solidus), °C 1320
1370
Specific Heat Capacity, J/kg-K 460
490
Thermal Conductivity, W/m-K 13
17
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
1.6
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 55
12
Density, g/cm3 8.4
7.6
Embodied Carbon, kg CO2/kg material 9.8
2.5
Embodied Energy, MJ/kg 140
37
Embodied Water, L/kg 260
170

Common Calculations

Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 23
26
Strength to Weight: Axial, points 21
23
Strength to Weight: Bending, points 19
21
Thermal Diffusivity, mm2/s 3.3
4.6
Thermal Shock Resistance, points 19
22

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
1.2 to 1.7
Carbon (C), % 0 to 0.080
0 to 0.12
Chromium (Cr), % 14 to 17
23 to 26
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 0 to 8.0
69.7 to 75.1
Manganese (Mn), % 2.0 to 2.7
0 to 1.0
Nickel (Ni), % 67 to 81.5
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.35
0.7 to 1.4
Sulfur (S), % 0 to 0.015
0 to 0.015
Titanium (Ti), % 2.5 to 3.5
0
Residuals, % 0 to 0.5
0