AWS ERNiCrFe-6 vs. EN 1.5536 Steel

AWS ERNiCrFe-6 belongs to the nickel alloys classification, while EN 1.5536 steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrFe-6 and the bottom bar is EN 1.5536 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Tensile Strength: Ultimate (UTS), MPa 630
460 to 1600

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Melting Completion (Liquidus), °C 1370
1460
Melting Onset (Solidus), °C 1320
1420
Specific Heat Capacity, J/kg-K 460
470
Thermal Conductivity, W/m-K 13
49
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 55
1.9
Density, g/cm3 8.4
7.8
Embodied Carbon, kg CO2/kg material 9.8
1.4
Embodied Energy, MJ/kg 140
19
Embodied Water, L/kg 260
48

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 21
16 to 57
Strength to Weight: Bending, points 19
17 to 39
Thermal Diffusivity, mm2/s 3.3
13
Thermal Shock Resistance, points 19
14 to 47

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0 to 0.080
0.25 to 0.3
Chromium (Cr), % 14 to 17
0 to 0.3
Copper (Cu), % 0 to 0.5
0 to 0.25
Iron (Fe), % 0 to 8.0
97.6 to 98.7
Manganese (Mn), % 2.0 to 2.7
0.9 to 1.2
Nickel (Ni), % 67 to 81.5
0
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 0.35
0.15 to 0.3
Sulfur (S), % 0 to 0.015
0 to 0.025
Titanium (Ti), % 2.5 to 3.5
0
Residuals, % 0 to 0.5
0