AWS ERNiCrFe-6 vs. EN 1.7386 Steel

AWS ERNiCrFe-6 belongs to the nickel alloys classification, while EN 1.7386 steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrFe-6 and the bottom bar is EN 1.7386 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 34
18 to 21
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
75
Tensile Strength: Ultimate (UTS), MPa 630
550 to 670

Thermal Properties

Latent Heat of Fusion, J/g 310
270
Melting Completion (Liquidus), °C 1370
1450
Melting Onset (Solidus), °C 1320
1410
Specific Heat Capacity, J/kg-K 460
480
Thermal Conductivity, W/m-K 13
26
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
9.0
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
10

Otherwise Unclassified Properties

Base Metal Price, % relative 55
6.5
Density, g/cm3 8.4
7.8
Embodied Carbon, kg CO2/kg material 9.8
2.0
Embodied Energy, MJ/kg 140
28
Embodied Water, L/kg 260
88

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 21
20 to 24
Strength to Weight: Bending, points 19
19 to 22
Thermal Diffusivity, mm2/s 3.3
6.9
Thermal Shock Resistance, points 19
15 to 18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.040
Carbon (C), % 0 to 0.080
0.080 to 0.15
Chromium (Cr), % 14 to 17
8.0 to 10
Copper (Cu), % 0 to 0.5
0 to 0.3
Iron (Fe), % 0 to 8.0
86.8 to 90.5
Manganese (Mn), % 2.0 to 2.7
0.3 to 0.6
Molybdenum (Mo), % 0
0.9 to 1.1
Nickel (Ni), % 67 to 81.5
0
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 0.35
0.25 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.010
Titanium (Ti), % 2.5 to 3.5
0
Residuals, % 0 to 0.5
0