AWS ERNiCrFe-6 vs. S31266 Stainless Steel

AWS ERNiCrFe-6 belongs to the nickel alloys classification, while S31266 stainless steel belongs to the iron alloys. They have 45% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrFe-6 and the bottom bar is S31266 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 34
40
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
81
Tensile Strength: Ultimate (UTS), MPa 630
860

Thermal Properties

Latent Heat of Fusion, J/g 310
310
Melting Completion (Liquidus), °C 1370
1470
Melting Onset (Solidus), °C 1320
1420
Specific Heat Capacity, J/kg-K 460
460
Thermal Conductivity, W/m-K 13
12
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
1.8
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 55
37
Density, g/cm3 8.4
8.2
Embodied Carbon, kg CO2/kg material 9.8
6.5
Embodied Energy, MJ/kg 140
89
Embodied Water, L/kg 260
220

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 21
29
Strength to Weight: Bending, points 19
24
Thermal Diffusivity, mm2/s 3.3
3.1
Thermal Shock Resistance, points 19
18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0 to 0.080
0 to 0.030
Chromium (Cr), % 14 to 17
23 to 25
Copper (Cu), % 0 to 0.5
1.0 to 2.5
Iron (Fe), % 0 to 8.0
34.1 to 46
Manganese (Mn), % 2.0 to 2.7
2.0 to 4.0
Molybdenum (Mo), % 0
5.2 to 6.2
Nickel (Ni), % 67 to 81.5
21 to 24
Nitrogen (N), % 0
0.35 to 0.6
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.020
Titanium (Ti), % 2.5 to 3.5
0
Tungsten (W), % 0
1.5 to 2.5
Residuals, % 0 to 0.5
0