AWS ERNiCrFe-6 vs. S35045 Stainless Steel

AWS ERNiCrFe-6 belongs to the nickel alloys classification, while S35045 stainless steel belongs to the iron alloys. They have 56% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrFe-6 and the bottom bar is S35045 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 34
39
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
78
Tensile Strength: Ultimate (UTS), MPa 630
540

Thermal Properties

Latent Heat of Fusion, J/g 310
310
Melting Completion (Liquidus), °C 1370
1390
Melting Onset (Solidus), °C 1320
1340
Specific Heat Capacity, J/kg-K 460
480
Thermal Conductivity, W/m-K 13
12
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 55
34
Density, g/cm3 8.4
8.0
Embodied Carbon, kg CO2/kg material 9.8
5.8
Embodied Energy, MJ/kg 140
83
Embodied Water, L/kg 260
230

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 21
19
Strength to Weight: Bending, points 19
19
Thermal Diffusivity, mm2/s 3.3
3.2
Thermal Shock Resistance, points 19
12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0.15 to 0.6
Carbon (C), % 0 to 0.080
0.060 to 0.1
Chromium (Cr), % 14 to 17
25 to 29
Copper (Cu), % 0 to 0.5
0 to 0.75
Iron (Fe), % 0 to 8.0
29.4 to 42.6
Manganese (Mn), % 2.0 to 2.7
0 to 1.5
Nickel (Ni), % 67 to 81.5
32 to 37
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.015
Titanium (Ti), % 2.5 to 3.5
0.15 to 0.6
Residuals, % 0 to 0.5
0