AWS ERNiCrFe-6 vs. S41425 Stainless Steel

AWS ERNiCrFe-6 belongs to the nickel alloys classification, while S41425 stainless steel belongs to the iron alloys. They have a modest 24% of their average alloy composition in common, which, by itself, doesn't mean much. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrFe-6 and the bottom bar is S41425 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 34
17
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
77
Tensile Strength: Ultimate (UTS), MPa 630
920

Thermal Properties

Latent Heat of Fusion, J/g 310
280
Melting Completion (Liquidus), °C 1370
1450
Melting Onset (Solidus), °C 1320
1410
Specific Heat Capacity, J/kg-K 460
470
Thermal Conductivity, W/m-K 13
16
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 55
13
Density, g/cm3 8.4
7.9
Embodied Carbon, kg CO2/kg material 9.8
2.9
Embodied Energy, MJ/kg 140
40
Embodied Water, L/kg 260
120

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 21
33
Strength to Weight: Bending, points 19
27
Thermal Diffusivity, mm2/s 3.3
4.4
Thermal Shock Resistance, points 19
33

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0 to 0.080
0 to 0.050
Chromium (Cr), % 14 to 17
12 to 15
Copper (Cu), % 0 to 0.5
0 to 0.3
Iron (Fe), % 0 to 8.0
74 to 81.9
Manganese (Mn), % 2.0 to 2.7
0.5 to 1.0
Molybdenum (Mo), % 0
1.5 to 2.0
Nickel (Ni), % 67 to 81.5
4.0 to 7.0
Nitrogen (N), % 0
0.060 to 0.12
Phosphorus (P), % 0 to 0.030
0 to 0.020
Silicon (Si), % 0 to 0.35
0 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.0050
Titanium (Ti), % 2.5 to 3.5
0
Residuals, % 0 to 0.5
0