AWS ERNiCrMo-3 vs. CC380H Copper-nickel

AWS ERNiCrMo-3 belongs to the nickel alloys classification, while CC380H copper-nickel belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrMo-3 and the bottom bar is CC380H copper-nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
120
Elongation at Break, % 34
26
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 79
47
Tensile Strength: Ultimate (UTS), MPa 870
310

Thermal Properties

Latent Heat of Fusion, J/g 330
220
Melting Completion (Liquidus), °C 1480
1130
Melting Onset (Solidus), °C 1430
1080
Specific Heat Capacity, J/kg-K 440
390
Thermal Conductivity, W/m-K 11
46
Thermal Expansion, µm/m-K 12
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.3
11
Electrical Conductivity: Equal Weight (Specific), % IACS 1.4
11

Otherwise Unclassified Properties

Base Metal Price, % relative 80
36
Density, g/cm3 8.6
8.9
Embodied Carbon, kg CO2/kg material 14
3.8
Embodied Energy, MJ/kg 190
58
Embodied Water, L/kg 290
300

Common Calculations

Stiffness to Weight: Axial, points 13
7.8
Stiffness to Weight: Bending, points 23
19
Strength to Weight: Axial, points 28
9.8
Strength to Weight: Bending, points 24
12
Thermal Diffusivity, mm2/s 2.8
13
Thermal Shock Resistance, points 25
11

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.4
0 to 0.010
Carbon (C), % 0 to 0.010
0
Chromium (Cr), % 20 to 23
0
Copper (Cu), % 0 to 0.5
84.5 to 89
Iron (Fe), % 0 to 5.0
1.0 to 1.8
Lead (Pb), % 0
0 to 0.030
Manganese (Mn), % 0 to 0.5
1.0 to 1.5
Molybdenum (Mo), % 8.0 to 10
0
Nickel (Ni), % 58 to 68.9
9.0 to 11
Niobium (Nb), % 3.2 to 4.2
0 to 1.0
Phosphorus (P), % 0 to 0.020
0
Silicon (Si), % 0 to 0.5
0 to 0.1
Sulfur (S), % 0 to 0.015
0
Titanium (Ti), % 0 to 0.4
0
Zinc (Zn), % 0
0 to 0.5
Residuals, % 0 to 0.5
0