AWS ERNiCrMo-3 vs. C14181 Copper

AWS ERNiCrMo-3 belongs to the nickel alloys classification, while C14181 copper belongs to the copper alloys. There are 22 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrMo-3 and the bottom bar is C14181 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
120
Elongation at Break, % 34
15
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 79
43
Tensile Strength: Ultimate (UTS), MPa 870
210

Thermal Properties

Latent Heat of Fusion, J/g 330
210
Melting Completion (Liquidus), °C 1480
1080
Melting Onset (Solidus), °C 1430
1080
Specific Heat Capacity, J/kg-K 440
390
Thermal Conductivity, W/m-K 11
380
Thermal Expansion, µm/m-K 12
17

Otherwise Unclassified Properties

Base Metal Price, % relative 80
31
Density, g/cm3 8.6
9.0
Embodied Carbon, kg CO2/kg material 14
2.6
Embodied Energy, MJ/kg 190
41
Embodied Water, L/kg 290
310

Common Calculations

Stiffness to Weight: Axial, points 13
7.2
Stiffness to Weight: Bending, points 23
18
Strength to Weight: Axial, points 28
6.5
Strength to Weight: Bending, points 24
8.8
Thermal Diffusivity, mm2/s 2.8
110
Thermal Shock Resistance, points 25
7.4

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.4
0
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0 to 0.010
0 to 0.0050
Chromium (Cr), % 20 to 23
0
Copper (Cu), % 0 to 0.5
99.9 to 100
Iron (Fe), % 0 to 5.0
0
Lead (Pb), % 0
0 to 0.0020
Manganese (Mn), % 0 to 0.5
0
Molybdenum (Mo), % 8.0 to 10
0
Nickel (Ni), % 58 to 68.9
0
Niobium (Nb), % 3.2 to 4.2
0
Phosphorus (P), % 0 to 0.020
0 to 0.0020
Silicon (Si), % 0 to 0.5
0
Sulfur (S), % 0 to 0.015
0
Titanium (Ti), % 0 to 0.4
0
Zinc (Zn), % 0
0 to 0.0020
Residuals, % 0 to 0.5
0