AWS ERNiCrMo-3 vs. C19700 Copper

AWS ERNiCrMo-3 belongs to the nickel alloys classification, while C19700 copper belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrMo-3 and the bottom bar is C19700 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
120
Elongation at Break, % 34
2.4 to 13
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 79
43
Tensile Strength: Ultimate (UTS), MPa 870
400 to 530

Thermal Properties

Latent Heat of Fusion, J/g 330
210
Melting Completion (Liquidus), °C 1480
1090
Melting Onset (Solidus), °C 1430
1040
Specific Heat Capacity, J/kg-K 440
390
Thermal Conductivity, W/m-K 11
250
Thermal Expansion, µm/m-K 12
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.3
86 to 88
Electrical Conductivity: Equal Weight (Specific), % IACS 1.4
87 to 89

Otherwise Unclassified Properties

Base Metal Price, % relative 80
30
Density, g/cm3 8.6
8.9
Embodied Carbon, kg CO2/kg material 14
2.6
Embodied Energy, MJ/kg 190
41
Embodied Water, L/kg 290
310

Common Calculations

Stiffness to Weight: Axial, points 13
7.2
Stiffness to Weight: Bending, points 23
18
Strength to Weight: Axial, points 28
12 to 16
Strength to Weight: Bending, points 24
14 to 16
Thermal Diffusivity, mm2/s 2.8
73
Thermal Shock Resistance, points 25
14 to 19

Alloy Composition

Aluminum (Al), % 0 to 0.4
0
Carbon (C), % 0 to 0.010
0
Chromium (Cr), % 20 to 23
0
Cobalt (Co), % 0
0 to 0.050
Copper (Cu), % 0 to 0.5
97.4 to 99.59
Iron (Fe), % 0 to 5.0
0.3 to 1.2
Lead (Pb), % 0
0 to 0.050
Magnesium (Mg), % 0
0.010 to 0.2
Manganese (Mn), % 0 to 0.5
0 to 0.050
Molybdenum (Mo), % 8.0 to 10
0
Nickel (Ni), % 58 to 68.9
0 to 0.050
Niobium (Nb), % 3.2 to 4.2
0
Phosphorus (P), % 0 to 0.020
0.1 to 0.4
Silicon (Si), % 0 to 0.5
0
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
0 to 0.2
Titanium (Ti), % 0 to 0.4
0
Zinc (Zn), % 0
0 to 0.2
Residuals, % 0 to 0.5
0 to 0.2