AWS ERNiCrMo-3 vs. C22600 Bronze

AWS ERNiCrMo-3 belongs to the nickel alloys classification, while C22600 bronze belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrMo-3 and the bottom bar is C22600 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 34
2.5 to 33
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 79
42
Tensile Strength: Ultimate (UTS), MPa 870
330 to 570

Thermal Properties

Latent Heat of Fusion, J/g 330
200
Melting Completion (Liquidus), °C 1480
1040
Melting Onset (Solidus), °C 1430
1000
Specific Heat Capacity, J/kg-K 440
390
Thermal Conductivity, W/m-K 11
170
Thermal Expansion, µm/m-K 12
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.3
40
Electrical Conductivity: Equal Weight (Specific), % IACS 1.4
42

Otherwise Unclassified Properties

Base Metal Price, % relative 80
28
Density, g/cm3 8.6
8.7
Embodied Carbon, kg CO2/kg material 14
2.6
Embodied Energy, MJ/kg 190
42
Embodied Water, L/kg 290
310

Common Calculations

Stiffness to Weight: Axial, points 13
7.2
Stiffness to Weight: Bending, points 23
19
Strength to Weight: Axial, points 28
11 to 18
Strength to Weight: Bending, points 24
12 to 18
Thermal Diffusivity, mm2/s 2.8
52
Thermal Shock Resistance, points 25
11 to 19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.4
0
Carbon (C), % 0 to 0.010
0
Chromium (Cr), % 20 to 23
0
Copper (Cu), % 0 to 0.5
86 to 89
Iron (Fe), % 0 to 5.0
0 to 0.050
Lead (Pb), % 0
0 to 0.050
Manganese (Mn), % 0 to 0.5
0
Molybdenum (Mo), % 8.0 to 10
0
Nickel (Ni), % 58 to 68.9
0
Niobium (Nb), % 3.2 to 4.2
0
Phosphorus (P), % 0 to 0.020
0
Silicon (Si), % 0 to 0.5
0
Sulfur (S), % 0 to 0.015
0
Titanium (Ti), % 0 to 0.4
0
Zinc (Zn), % 0
10.7 to 14
Residuals, % 0 to 0.5
0 to 0.2