MakeItFrom.com
Menu (ESC)

AWS ERNiCrMo-3 vs. C82600 Copper

AWS ERNiCrMo-3 belongs to the nickel alloys classification, while C82600 copper belongs to the copper alloys. There are 23 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrMo-3 and the bottom bar is C82600 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
120
Elongation at Break, % 34
1.0 to 20
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 79
46
Tensile Strength: Ultimate (UTS), MPa 870
570 to 1140

Thermal Properties

Latent Heat of Fusion, J/g 330
240
Melting Completion (Liquidus), °C 1480
950
Melting Onset (Solidus), °C 1430
860
Specific Heat Capacity, J/kg-K 440
390
Thermal Conductivity, W/m-K 11
130
Thermal Expansion, µm/m-K 12
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.3
19
Electrical Conductivity: Equal Weight (Specific), % IACS 1.4
20

Otherwise Unclassified Properties

Density, g/cm3 8.6
8.7
Embodied Carbon, kg CO2/kg material 14
11
Embodied Energy, MJ/kg 190
180
Embodied Water, L/kg 290
310

Common Calculations

Stiffness to Weight: Axial, points 13
7.8
Stiffness to Weight: Bending, points 23
19
Strength to Weight: Axial, points 28
18 to 36
Strength to Weight: Bending, points 24
17 to 28
Thermal Diffusivity, mm2/s 2.8
37
Thermal Shock Resistance, points 25
19 to 39

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.4
0 to 0.15
Beryllium (Be), % 0
2.3 to 2.6
Carbon (C), % 0 to 0.010
0
Chromium (Cr), % 20 to 23
0 to 0.1
Cobalt (Co), % 0
0.35 to 0.65
Copper (Cu), % 0 to 0.5
94.9 to 97.2
Iron (Fe), % 0 to 5.0
0 to 0.25
Lead (Pb), % 0
0 to 0.020
Manganese (Mn), % 0 to 0.5
0
Molybdenum (Mo), % 8.0 to 10
0
Nickel (Ni), % 58 to 68.9
0 to 0.2
Niobium (Nb), % 3.2 to 4.2
0
Phosphorus (P), % 0 to 0.020
0
Silicon (Si), % 0 to 0.5
0.2 to 0.35
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
0 to 0.1
Titanium (Ti), % 0 to 0.4
0 to 0.12
Zinc (Zn), % 0
0 to 0.1
Residuals, % 0 to 0.5
0 to 0.5