AWS ERNiMo-3 vs. Nickel 684
Both AWS ERNiMo-3 and nickel 684 are nickel alloys. They have 67% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is AWS ERNiMo-3 and the bottom bar is nickel 684.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 200 |
| Poisson's Ratio | 0.3 | |
| 0.29 |
| Shear Modulus, GPa | 83 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 770 | |
| 1190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 320 |
| Melting Completion (Liquidus), °C | 1600 | |
| 1370 |
| Melting Onset (Solidus), °C | 1540 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 470 |
| Thermal Expansion, µm/m-K | 11 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 70 | |
| 75 |
| Density, g/cm3 | 9.1 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 15 | |
| 10 |
| Embodied Energy, MJ/kg | 190 | |
| 140 |
| Embodied Water, L/kg | 270 | |
| 360 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 22 | |
| 23 |
| Strength to Weight: Axial, points | 24 | |
| 40 |
| Strength to Weight: Bending, points | 21 | |
| 30 |
| Thermal Shock Resistance, points | 24 | |
| 34 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 2.5 to 3.3 |
| Boron (B), % | 0 | |
| 0.0030 to 0.010 |
| Carbon (C), % | 0 to 0.12 | |
| 0 to 0.15 |
| Chromium (Cr), % | 4.0 to 6.0 | |
| 15 to 20 |
| Cobalt (Co), % | 0 to 2.5 | |
| 13 to 20 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 to 0.15 |
| Iron (Fe), % | 4.0 to 7.0 | |
| 0 to 4.0 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 0.75 |
| Molybdenum (Mo), % | 23 to 26 | |
| 3.0 to 5.0 |
| Nickel (Ni), % | 53.7 to 69 | |
| 42.7 to 64 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.75 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 2.5 to 3.3 |
| Tungsten (W), % | 0 to 1.0 | |
| 0 |
| Vanadium (V), % | 0 to 0.6 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |