AWS ERNiMo-3 vs. N06007 Nickel

Both AWS ERNiMo-3 and N06007 nickel are nickel alloys. They have 64% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiMo-3 and the bottom bar is N06007 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
200
Poisson's Ratio 0.3
0.29
Shear Modulus, GPa 83
79
Tensile Strength: Ultimate (UTS), MPa 770
690

Thermal Properties

Latent Heat of Fusion, J/g 320
320
Melting Completion (Liquidus), °C 1600
1340
Melting Onset (Solidus), °C 1540
1260
Specific Heat Capacity, J/kg-K 400
450
Thermal Expansion, µm/m-K 11
14

Otherwise Unclassified Properties

Base Metal Price, % relative 70
60
Density, g/cm3 9.1
8.4
Embodied Carbon, kg CO2/kg material 15
10
Embodied Energy, MJ/kg 190
140
Embodied Water, L/kg 270
260

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 22
23
Strength to Weight: Axial, points 24
23
Strength to Weight: Bending, points 21
21
Thermal Shock Resistance, points 24
18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0 to 0.12
0 to 0.050
Chromium (Cr), % 4.0 to 6.0
21 to 23.5
Cobalt (Co), % 0 to 2.5
0 to 2.5
Copper (Cu), % 0 to 0.5
1.5 to 2.5
Iron (Fe), % 4.0 to 7.0
18 to 21
Manganese (Mn), % 0 to 1.0
1.0 to 2.0
Molybdenum (Mo), % 23 to 26
5.5 to 7.5
Nickel (Ni), % 53.7 to 69
36.1 to 51.1
Niobium (Nb), % 0
1.8 to 2.5
Nitrogen (N), % 0
0.15 to 0.25
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0 to 1.0
0 to 1.0
Vanadium (V), % 0 to 0.6
0
Residuals, % 0 to 0.5
0