AWS ERNiMo-3 vs. N08024 Nickel

Both AWS ERNiMo-3 and N08024 nickel are nickel alloys. They have 53% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiMo-3 and the bottom bar is N08024 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
200
Poisson's Ratio 0.3
0.28
Shear Modulus, GPa 83
79
Tensile Strength: Ultimate (UTS), MPa 770
620

Thermal Properties

Latent Heat of Fusion, J/g 320
310
Melting Completion (Liquidus), °C 1600
1430
Melting Onset (Solidus), °C 1540
1380
Specific Heat Capacity, J/kg-K 400
460
Thermal Expansion, µm/m-K 11
15

Otherwise Unclassified Properties

Base Metal Price, % relative 70
41
Density, g/cm3 9.1
8.2
Embodied Carbon, kg CO2/kg material 15
7.2
Embodied Energy, MJ/kg 190
99
Embodied Water, L/kg 270
230

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 22
24
Strength to Weight: Axial, points 24
21
Strength to Weight: Bending, points 21
20
Thermal Shock Resistance, points 24
15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0 to 0.12
0 to 0.030
Chromium (Cr), % 4.0 to 6.0
22.5 to 25
Cobalt (Co), % 0 to 2.5
0
Copper (Cu), % 0 to 0.5
0.5 to 1.5
Iron (Fe), % 4.0 to 7.0
26.6 to 38.4
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 23 to 26
3.5 to 5.0
Nickel (Ni), % 53.7 to 69
35 to 40
Niobium (Nb), % 0
0.15 to 0.35
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.035
Tungsten (W), % 0 to 1.0
0
Vanadium (V), % 0 to 0.6
0
Residuals, % 0 to 0.5
0