AWS ERNiMo-3 vs. N08120 Nickel

Both AWS ERNiMo-3 and N08120 nickel are nickel alloys. They have 52% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiMo-3 and the bottom bar is N08120 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
200
Poisson's Ratio 0.3
0.28
Shear Modulus, GPa 83
79
Tensile Strength: Ultimate (UTS), MPa 770
700

Thermal Properties

Latent Heat of Fusion, J/g 320
310
Melting Completion (Liquidus), °C 1600
1420
Melting Onset (Solidus), °C 1540
1370
Specific Heat Capacity, J/kg-K 400
470
Thermal Expansion, µm/m-K 11
14

Otherwise Unclassified Properties

Base Metal Price, % relative 70
45
Density, g/cm3 9.1
8.2
Embodied Carbon, kg CO2/kg material 15
7.2
Embodied Energy, MJ/kg 190
100
Embodied Water, L/kg 270
240

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 22
24
Strength to Weight: Axial, points 24
24
Strength to Weight: Bending, points 21
21
Thermal Shock Resistance, points 24
17

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.4
Boron (B), % 0
0 to 0.010
Carbon (C), % 0 to 0.12
0.020 to 0.1
Chromium (Cr), % 4.0 to 6.0
23 to 27
Cobalt (Co), % 0 to 2.5
0 to 3.0
Copper (Cu), % 0 to 0.5
0 to 0.5
Iron (Fe), % 4.0 to 7.0
21 to 41.4
Manganese (Mn), % 0 to 1.0
0 to 1.5
Molybdenum (Mo), % 23 to 26
0 to 2.5
Nickel (Ni), % 53.7 to 69
35 to 39
Niobium (Nb), % 0
0.4 to 0.9
Nitrogen (N), % 0
0.15 to 0.3
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Titanium (Ti), % 0
0 to 0.2
Tungsten (W), % 0 to 1.0
0 to 2.5
Vanadium (V), % 0 to 0.6
0
Residuals, % 0 to 0.5
0