AWS ERTi-12 vs. EN 1.5520 Steel

AWS ERTi-12 belongs to the titanium alloys classification, while EN 1.5520 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AWS ERTi-12 and the bottom bar is EN 1.5520 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
190
Elongation at Break, % 12
11 to 21
Fatigue Strength, MPa 200
210 to 300
Poisson's Ratio 0.32
0.29
Shear Modulus, GPa 41
73
Tensile Strength: Ultimate (UTS), MPa 480
410 to 1410
Tensile Strength: Yield (Proof), MPa 340
300 to 480

Thermal Properties

Latent Heat of Fusion, J/g 420
250
Maximum Temperature: Mechanical, °C 320
400
Melting Completion (Liquidus), °C 1670
1460
Melting Onset (Solidus), °C 1620
1420
Specific Heat Capacity, J/kg-K 540
470
Thermal Conductivity, W/m-K 21
50
Thermal Expansion, µm/m-K 8.7
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.6
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 7.1
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 37
1.9
Density, g/cm3 4.5
7.8
Embodied Carbon, kg CO2/kg material 31
1.4
Embodied Energy, MJ/kg 510
19
Embodied Water, L/kg 110
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 52
42 to 230
Resilience: Unit (Modulus of Resilience), kJ/m3 550
240 to 600
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 35
24
Strength to Weight: Axial, points 30
15 to 50
Strength to Weight: Bending, points 30
16 to 36
Thermal Diffusivity, mm2/s 8.7
13
Thermal Shock Resistance, points 37
12 to 41

Alloy Composition

Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0 to 0.030
0.15 to 0.2
Chromium (Cr), % 0
0 to 0.3
Copper (Cu), % 0
0 to 0.25
Hydrogen (H), % 0 to 0.0080
0
Iron (Fe), % 0 to 0.15
97.7 to 98.9
Manganese (Mn), % 0
0.9 to 1.2
Molybdenum (Mo), % 0.2 to 0.4
0
Nickel (Ni), % 0.060 to 0.090
0
Nitrogen (N), % 0 to 0.015
0
Oxygen (O), % 0.080 to 0.16
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0
0 to 0.3
Sulfur (S), % 0
0 to 0.025
Titanium (Ti), % 99.147 to 99.66
0