AWS ERTi-12 vs. EN 1.8872 Steel

AWS ERTi-12 belongs to the titanium alloys classification, while EN 1.8872 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AWS ERTi-12 and the bottom bar is EN 1.8872 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
190
Elongation at Break, % 12
21
Fatigue Strength, MPa 200
310
Poisson's Ratio 0.32
0.29
Shear Modulus, GPa 41
73
Tensile Strength: Ultimate (UTS), MPa 480
610
Tensile Strength: Yield (Proof), MPa 340
450

Thermal Properties

Latent Heat of Fusion, J/g 420
250
Maximum Temperature: Mechanical, °C 320
410
Melting Completion (Liquidus), °C 1670
1460
Melting Onset (Solidus), °C 1620
1420
Specific Heat Capacity, J/kg-K 540
470
Thermal Conductivity, W/m-K 21
39
Thermal Expansion, µm/m-K 8.7
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.6
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 7.1
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 37
2.8
Density, g/cm3 4.5
7.9
Embodied Carbon, kg CO2/kg material 31
1.7
Embodied Energy, MJ/kg 510
22
Embodied Water, L/kg 110
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 52
120
Resilience: Unit (Modulus of Resilience), kJ/m3 550
530
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 35
24
Strength to Weight: Axial, points 30
22
Strength to Weight: Bending, points 30
20
Thermal Diffusivity, mm2/s 8.7
10
Thermal Shock Resistance, points 37
18

Alloy Composition

Boron (B), % 0
0 to 0.0050
Carbon (C), % 0 to 0.030
0 to 0.18
Chromium (Cr), % 0
0 to 0.5
Copper (Cu), % 0
0 to 0.3
Hydrogen (H), % 0 to 0.0080
0
Iron (Fe), % 0 to 0.15
95.1 to 100
Manganese (Mn), % 0
0 to 1.7
Molybdenum (Mo), % 0.2 to 0.4
0 to 0.5
Nickel (Ni), % 0.060 to 0.090
0 to 1.0
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0 to 0.015
0 to 0.015
Oxygen (O), % 0.080 to 0.16
0
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 0
0 to 0.5
Sulfur (S), % 0
0 to 0.0080
Titanium (Ti), % 99.147 to 99.66
0 to 0.030
Vanadium (V), % 0
0 to 0.080
Zirconium (Zr), % 0
0 to 0.050