AWS ERTi-5 vs. EN 1.4513 Stainless Steel

AWS ERTi-5 belongs to the titanium alloys classification, while EN 1.4513 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AWS ERTi-5 and the bottom bar is EN 1.4513 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
200
Elongation at Break, % 10
26
Fatigue Strength, MPa 470
170
Poisson's Ratio 0.32
0.28
Shear Modulus, GPa 40
77
Tensile Strength: Ultimate (UTS), MPa 900
480
Tensile Strength: Yield (Proof), MPa 830
240

Thermal Properties

Latent Heat of Fusion, J/g 410
280
Maximum Temperature: Mechanical, °C 340
880
Melting Completion (Liquidus), °C 1610
1450
Melting Onset (Solidus), °C 1560
1410
Specific Heat Capacity, J/kg-K 560
480
Thermal Conductivity, W/m-K 7.1
25
Thermal Expansion, µm/m-K 9.6
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.0
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 36
10
Density, g/cm3 4.4
7.7
Embodied Carbon, kg CO2/kg material 38
2.5
Embodied Energy, MJ/kg 610
35
Embodied Water, L/kg 200
120

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 87
100
Resilience: Unit (Modulus of Resilience), kJ/m3 3250
150
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 35
25
Strength to Weight: Axial, points 56
17
Strength to Weight: Bending, points 46
18
Thermal Diffusivity, mm2/s 2.9
6.8
Thermal Shock Resistance, points 63
17

Alloy Composition

Aluminum (Al), % 5.5 to 6.8
0
Carbon (C), % 0 to 0.050
0 to 0.025
Chromium (Cr), % 0
16 to 18
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0 to 0.22
77.7 to 83.1
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
0.8 to 1.4
Nitrogen (N), % 0 to 0.030
0 to 0.020
Oxygen (O), % 0.12 to 0.2
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.015
Titanium (Ti), % 88.2 to 90.9
0.15 to 0.8
Vanadium (V), % 3.5 to 4.5
0