AWS ERTi-7 vs. 2618A Aluminum
AWS ERTi-7 belongs to the titanium alloys classification, while 2618A aluminum belongs to the aluminum alloys. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is AWS ERTi-7 and the bottom bar is 2618A aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 72 |
| Elongation at Break, % | 20 | |
| 4.5 |
| Fatigue Strength, MPa | 190 | |
| 120 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 40 | |
| 27 |
| Tensile Strength: Ultimate (UTS), MPa | 340 | |
| 440 |
| Tensile Strength: Yield (Proof), MPa | 280 | |
| 410 |
Thermal Properties
| Latent Heat of Fusion, J/g | 420 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 320 | |
| 230 |
| Melting Completion (Liquidus), °C | 1670 | |
| 670 |
| Melting Onset (Solidus), °C | 1620 | |
| 560 |
| Specific Heat Capacity, J/kg-K | 540 | |
| 880 |
| Thermal Conductivity, W/m-K | 21 | |
| 150 |
| Thermal Expansion, µm/m-K | 8.7 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.6 | |
| 37 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.3 | |
| 110 |
Otherwise Unclassified Properties
| Density, g/cm3 | 4.5 | |
| 3.0 |
| Embodied Carbon, kg CO2/kg material | 47 | |
| 8.4 |
| Embodied Energy, MJ/kg | 800 | |
| 150 |
| Embodied Water, L/kg | 470 | |
| 1150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 64 | |
| 19 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 360 | |
| 1180 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 35 | |
| 47 |
| Strength to Weight: Axial, points | 21 | |
| 41 |
| Strength to Weight: Bending, points | 24 | |
| 44 |
| Thermal Diffusivity, mm2/s | 8.8 | |
| 59 |
| Thermal Shock Resistance, points | 26 | |
| 19 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 | |
| 91.5 to 95.2 |
| Carbon (C), % | 0 to 0.030 | |
| 0 |
| Copper (Cu), % | 0 | |
| 1.8 to 2.7 |
| Hydrogen (H), % | 0 to 0.0080 | |
| 0 |
| Iron (Fe), % | 0 to 0.12 | |
| 0.9 to 1.4 |
| Magnesium (Mg), % | 0 | |
| 1.2 to 1.8 |
| Manganese (Mn), % | 0 | |
| 0 to 0.25 |
| Nickel (Ni), % | 0 | |
| 0.8 to 1.4 |
| Nitrogen (N), % | 0 to 0.015 | |
| 0 |
| Oxygen (O), % | 0.080 to 0.16 | |
| 0 |
| Palladium (Pd), % | 0.12 to 0.25 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0.15 to 0.25 |
| Titanium (Ti), % | 99.417 to 99.8 | |
| 0 to 0.2 |
| Zinc (Zn), % | 0 | |
| 0 to 0.15 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.25 |
| Residuals, % | 0 | |
| 0 to 0.15 |