AWS ERTi-7 vs. C18600 Copper
AWS ERTi-7 belongs to the titanium alloys classification, while C18600 copper belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is AWS ERTi-7 and the bottom bar is C18600 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 120 |
| Elongation at Break, % | 20 | |
| 8.0 to 11 |
| Poisson's Ratio | 0.32 | |
| 0.34 |
| Shear Modulus, GPa | 40 | |
| 44 |
| Tensile Strength: Ultimate (UTS), MPa | 340 | |
| 520 to 580 |
| Tensile Strength: Yield (Proof), MPa | 280 | |
| 500 to 520 |
Thermal Properties
| Latent Heat of Fusion, J/g | 420 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 320 | |
| 200 |
| Melting Completion (Liquidus), °C | 1670 | |
| 1090 |
| Melting Onset (Solidus), °C | 1620 | |
| 1070 |
| Specific Heat Capacity, J/kg-K | 540 | |
| 390 |
| Thermal Conductivity, W/m-K | 21 | |
| 280 |
| Thermal Expansion, µm/m-K | 8.7 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.6 | |
| 70 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.3 | |
| 71 |
Otherwise Unclassified Properties
| Density, g/cm3 | 4.5 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 47 | |
| 2.9 |
| Embodied Energy, MJ/kg | 800 | |
| 46 |
| Embodied Water, L/kg | 470 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 64 | |
| 44 to 58 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 360 | |
| 1060 to 1180 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 35 | |
| 18 |
| Strength to Weight: Axial, points | 21 | |
| 16 to 18 |
| Strength to Weight: Bending, points | 24 | |
| 16 to 17 |
| Thermal Diffusivity, mm2/s | 8.8 | |
| 81 |
| Thermal Shock Resistance, points | 26 | |
| 19 to 20 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0 to 0.030 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0.1 to 1.0 |
| Cobalt (Co), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 0 | |
| 96.5 to 99.55 |
| Hydrogen (H), % | 0 to 0.0080 | |
| 0 |
| Iron (Fe), % | 0 to 0.12 | |
| 0.25 to 0.8 |
| Nickel (Ni), % | 0 | |
| 0 to 0.25 |
| Nitrogen (N), % | 0 to 0.015 | |
| 0 |
| Oxygen (O), % | 0.080 to 0.16 | |
| 0 |
| Palladium (Pd), % | 0.12 to 0.25 | |
| 0 |
| Titanium (Ti), % | 99.417 to 99.8 | |
| 0.050 to 0.5 |
| Zirconium (Zr), % | 0 | |
| 0.050 to 0.4 |
| Residuals, % | 0 | |
| 0 to 0.5 |