AZ31B Magnesium vs. AISI 201LN Stainless Steel
AZ31B magnesium belongs to the magnesium alloys classification, while AISI 201LN stainless steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is AZ31B magnesium and the bottom bar is AISI 201LN stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 45 | |
| 200 |
| Elongation at Break, % | 5.6 to 12 | |
| 25 to 51 |
| Fatigue Strength, MPa | 100 to 120 | |
| 340 to 540 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 17 | |
| 77 |
| Shear Strength, MPa | 130 to 160 | |
| 530 to 680 |
| Tensile Strength: Ultimate (UTS), MPa | 240 to 270 | |
| 740 to 1060 |
| Tensile Strength: Yield (Proof), MPa | 120 to 180 | |
| 350 to 770 |
Thermal Properties
| Latent Heat of Fusion, J/g | 350 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 150 | |
| 880 |
| Melting Completion (Liquidus), °C | 600 | |
| 1410 |
| Melting Onset (Solidus), °C | 600 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 990 | |
| 480 |
| Thermal Conductivity, W/m-K | 100 | |
| 15 |
| Thermal Expansion, µm/m-K | 26 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 18 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 95 | |
| 2.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 12 |
| Density, g/cm3 | 1.7 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 23 | |
| 2.6 |
| Embodied Energy, MJ/kg | 160 | |
| 38 |
| Embodied Water, L/kg | 970 | |
| 140 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 13 to 25 | |
| 230 to 310 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 to 370 | |
| 310 to 1520 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 70 | |
| 25 |
| Strength to Weight: Axial, points | 39 to 44 | |
| 27 to 38 |
| Strength to Weight: Bending, points | 50 to 55 | |
| 24 to 30 |
| Thermal Diffusivity, mm2/s | 62 | |
| 4.0 |
| Thermal Shock Resistance, points | 14 to 16 | |
| 16 to 23 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 2.4 to 3.6 | |
| 0 |
| Calcium (Ca), % | 0 to 0.040 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 | |
| 16 to 17.5 |
| Copper (Cu), % | 0 to 0.050 | |
| 0 to 1.0 |
| Iron (Fe), % | 0 to 0.050 | |
| 67.9 to 73.5 |
| Magnesium (Mg), % | 93.6 to 97.1 | |
| 0 |
| Manganese (Mn), % | 0.050 to 1.0 | |
| 6.4 to 7.5 |
| Nickel (Ni), % | 0 to 0.0050 | |
| 4.0 to 5.0 |
| Nitrogen (N), % | 0 | |
| 0.1 to 0.25 |
| Phosphorus (P), % | 0 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.75 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Zinc (Zn), % | 0.5 to 1.5 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 |