AZ31B Magnesium vs. EN AC-51500 Aluminum
AZ31B magnesium belongs to the magnesium alloys classification, while EN AC-51500 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is AZ31B magnesium and the bottom bar is EN AC-51500 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 45 | |
| 68 |
| Elongation at Break, % | 5.6 to 12 | |
| 5.6 |
| Fatigue Strength, MPa | 100 to 120 | |
| 120 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 17 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 240 to 270 | |
| 280 |
| Tensile Strength: Yield (Proof), MPa | 120 to 180 | |
| 160 |
Thermal Properties
| Latent Heat of Fusion, J/g | 350 | |
| 430 |
| Maximum Temperature: Mechanical, °C | 150 | |
| 170 |
| Melting Completion (Liquidus), °C | 600 | |
| 630 |
| Melting Onset (Solidus), °C | 600 | |
| 590 |
| Specific Heat Capacity, J/kg-K | 990 | |
| 910 |
| Thermal Conductivity, W/m-K | 100 | |
| 120 |
| Thermal Expansion, µm/m-K | 26 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 18 | |
| 26 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 95 | |
| 88 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 9.5 |
| Density, g/cm3 | 1.7 | |
| 2.6 |
| Embodied Carbon, kg CO2/kg material | 23 | |
| 9.0 |
| Embodied Energy, MJ/kg | 160 | |
| 150 |
| Embodied Water, L/kg | 970 | |
| 1150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 13 to 25 | |
| 13 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 to 370 | |
| 190 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 70 | |
| 52 |
| Strength to Weight: Axial, points | 39 to 44 | |
| 29 |
| Strength to Weight: Bending, points | 50 to 55 | |
| 36 |
| Thermal Diffusivity, mm2/s | 62 | |
| 49 |
| Thermal Shock Resistance, points | 14 to 16 | |
| 13 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 2.4 to 3.6 | |
| 89.8 to 93.1 |
| Calcium (Ca), % | 0 to 0.040 | |
| 0 |
| Copper (Cu), % | 0 to 0.050 | |
| 0 to 0.050 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 to 0.25 |
| Magnesium (Mg), % | 93.6 to 97.1 | |
| 4.7 to 6.0 |
| Manganese (Mn), % | 0.050 to 1.0 | |
| 0.4 to 0.8 |
| Nickel (Ni), % | 0 to 0.0050 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 1.8 to 2.6 |
| Titanium (Ti), % | 0 | |
| 0 to 0.25 |
| Zinc (Zn), % | 0.5 to 1.5 | |
| 0 to 0.070 |
| Residuals, % | 0 to 0.3 | |