AZ61A Magnesium vs. 5082 Aluminum
AZ61A magnesium belongs to the magnesium alloys classification, while 5082 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is AZ61A magnesium and the bottom bar is 5082 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 45 | |
| 67 |
| Elongation at Break, % | 11 | |
| 1.1 |
| Fatigue Strength, MPa | 130 | |
| 110 to 130 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 17 | |
| 25 |
| Shear Strength, MPa | 150 | |
| 210 to 230 |
| Tensile Strength: Ultimate (UTS), MPa | 280 | |
| 380 to 400 |
| Tensile Strength: Yield (Proof), MPa | 170 | |
| 300 to 340 |
Thermal Properties
| Latent Heat of Fusion, J/g | 350 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 180 |
| Melting Completion (Liquidus), °C | 600 | |
| 640 |
| Melting Onset (Solidus), °C | 530 | |
| 560 |
| Specific Heat Capacity, J/kg-K | 990 | |
| 910 |
| Thermal Conductivity, W/m-K | 79 | |
| 130 |
| Thermal Expansion, µm/m-K | 27 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 12 | |
| 32 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 62 | |
| 110 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 9.5 |
| Density, g/cm3 | 1.7 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 23 | |
| 8.9 |
| Embodied Energy, MJ/kg | 160 | |
| 150 |
| Embodied Water, L/kg | 980 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 27 | |
| 4.0 to 4.3 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 310 | |
| 670 to 870 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 69 | |
| 51 |
| Strength to Weight: Axial, points | 46 | |
| 39 to 41 |
| Strength to Weight: Bending, points | 56 | |
| 43 to 45 |
| Thermal Diffusivity, mm2/s | 47 | |
| 54 |
| Thermal Shock Resistance, points | 17 | |
| 17 to 18 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 5.5 to 7.2 | |
| 93.5 to 96 |
| Chromium (Cr), % | 0 | |
| 0 to 0.15 |
| Copper (Cu), % | 0 to 0.050 | |
| 0 to 0.15 |
| Iron (Fe), % | 0 to 0.0050 | |
| 0 to 0.35 |
| Magnesium (Mg), % | 90.3 to 93.9 | |
| 4.0 to 5.0 |
| Manganese (Mn), % | 0.15 to 0.5 | |
| 0 to 0.15 |
| Nickel (Ni), % | 0 to 0.0050 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.2 |
| Titanium (Ti), % | 0 | |
| 0 to 0.1 |
| Zinc (Zn), % | 0.4 to 1.5 | |
| 0 to 0.25 |
| Residuals, % | 0 to 0.3 | |
| 0 to 0.15 |