AZ61A Magnesium vs. ACI-ASTM CD4MCu Steel

AZ61A magnesium belongs to the magnesium alloys classification, while ACI-ASTM CD4MCu steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AZ61A magnesium and the bottom bar is ACI-ASTM CD4MCu steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
200
Elongation at Break, % 11
18
Fatigue Strength, MPa 130
340
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 17
79
Tensile Strength: Ultimate (UTS), MPa 280
770
Tensile Strength: Yield (Proof), MPa 170
550

Thermal Properties

Latent Heat of Fusion, J/g 350
300
Maximum Temperature: Mechanical, °C 120
1100
Melting Completion (Liquidus), °C 600
1430
Melting Onset (Solidus), °C 530
1380
Specific Heat Capacity, J/kg-K 990
480
Thermal Conductivity, W/m-K 79
17
Thermal Expansion, µm/m-K 27
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 12
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 62
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 12
18
Density, g/cm3 1.7
7.8
Embodied Carbon, kg CO2/kg material 23
3.5
Embodied Energy, MJ/kg 160
49
Embodied Water, L/kg 980
180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 27
130
Resilience: Unit (Modulus of Resilience), kJ/m3 310
760
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 69
25
Strength to Weight: Axial, points 46
28
Strength to Weight: Bending, points 56
24
Thermal Diffusivity, mm2/s 47
4.5
Thermal Shock Resistance, points 17
21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.5 to 7.2
0
Carbon (C), % 0
0 to 0.040
Chromium (Cr), % 0
24.5 to 26.5
Copper (Cu), % 0 to 0.050
2.8 to 3.3
Iron (Fe), % 0 to 0.0050
59.9 to 66.3
Magnesium (Mg), % 90.3 to 93.9
0
Manganese (Mn), % 0.15 to 0.5
0 to 1.0
Molybdenum (Mo), % 0
1.8 to 2.3
Nickel (Ni), % 0 to 0.0050
4.8 to 6.0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.1
0 to 1.0
Sulfur (S), % 0
0 to 0.040
Zinc (Zn), % 0.4 to 1.5
0
Residuals, % 0 to 0.3
0