AZ61A Magnesium vs. EN 1.0528 Steel

AZ61A magnesium belongs to the magnesium alloys classification, while EN 1.0528 steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AZ61A magnesium and the bottom bar is EN 1.0528 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
190
Elongation at Break, % 11
20
Fatigue Strength, MPa 130
180
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 17
73
Shear Strength, MPa 150
320
Tensile Strength: Ultimate (UTS), MPa 280
520
Tensile Strength: Yield (Proof), MPa 170
260

Thermal Properties

Latent Heat of Fusion, J/g 350
250
Maximum Temperature: Mechanical, °C 120
400
Melting Completion (Liquidus), °C 600
1460
Melting Onset (Solidus), °C 530
1420
Specific Heat Capacity, J/kg-K 990
470
Thermal Conductivity, W/m-K 79
48
Thermal Expansion, µm/m-K 27
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 12
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 62
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 12
2.1
Density, g/cm3 1.7
7.8
Embodied Carbon, kg CO2/kg material 23
1.4
Embodied Energy, MJ/kg 160
19
Embodied Water, L/kg 980
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 27
88
Resilience: Unit (Modulus of Resilience), kJ/m3 310
180
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 69
24
Strength to Weight: Axial, points 46
18
Strength to Weight: Bending, points 56
18
Thermal Diffusivity, mm2/s 47
13
Thermal Shock Resistance, points 17
16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.5 to 7.2
0
Carbon (C), % 0
0.27 to 0.34
Chromium (Cr), % 0
0 to 0.4
Copper (Cu), % 0 to 0.050
0
Iron (Fe), % 0 to 0.0050
97.5 to 99.23
Magnesium (Mg), % 90.3 to 93.9
0
Manganese (Mn), % 0.15 to 0.5
0.5 to 0.8
Molybdenum (Mo), % 0
0 to 0.1
Nickel (Ni), % 0 to 0.0050
0 to 0.4
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0 to 0.1
0 to 0.4
Sulfur (S), % 0
0 to 0.045
Zinc (Zn), % 0.4 to 1.5
0
Residuals, % 0 to 0.3
0