AZ61A Magnesium vs. EN 1.4958 Stainless Steel

AZ61A magnesium belongs to the magnesium alloys classification, while EN 1.4958 stainless steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AZ61A magnesium and the bottom bar is EN 1.4958 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
200
Elongation at Break, % 11
40
Fatigue Strength, MPa 130
170
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 17
77
Shear Strength, MPa 150
430
Tensile Strength: Ultimate (UTS), MPa 280
630
Tensile Strength: Yield (Proof), MPa 170
190

Thermal Properties

Latent Heat of Fusion, J/g 350
300
Maximum Temperature: Mechanical, °C 120
1090
Melting Completion (Liquidus), °C 600
1400
Melting Onset (Solidus), °C 530
1350
Specific Heat Capacity, J/kg-K 990
480
Thermal Conductivity, W/m-K 79
12
Thermal Expansion, µm/m-K 27
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 12
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 62
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 12
30
Density, g/cm3 1.7
8.0
Embodied Carbon, kg CO2/kg material 23
5.3
Embodied Energy, MJ/kg 160
75
Embodied Water, L/kg 980
200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 27
190
Resilience: Unit (Modulus of Resilience), kJ/m3 310
95
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 69
24
Strength to Weight: Axial, points 46
22
Strength to Weight: Bending, points 56
20
Thermal Diffusivity, mm2/s 47
3.2
Thermal Shock Resistance, points 17
15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.5 to 7.2
0.2 to 0.5
Carbon (C), % 0
0.030 to 0.080
Chromium (Cr), % 0
19 to 22
Cobalt (Co), % 0
0 to 0.5
Copper (Cu), % 0 to 0.050
0 to 0.5
Iron (Fe), % 0 to 0.0050
41.1 to 50.6
Magnesium (Mg), % 90.3 to 93.9
0
Manganese (Mn), % 0.15 to 0.5
0 to 1.5
Nickel (Ni), % 0 to 0.0050
30 to 32.5
Niobium (Nb), % 0
0 to 0.1
Nitrogen (N), % 0
0 to 0.030
Phosphorus (P), % 0
0 to 0.015
Silicon (Si), % 0 to 0.1
0 to 0.7
Sulfur (S), % 0
0 to 0.010
Titanium (Ti), % 0
0.2 to 0.5
Zinc (Zn), % 0.4 to 1.5
0
Residuals, % 0 to 0.3
0