AZ61A Magnesium vs. EN 1.8881 Steel

AZ61A magnesium belongs to the magnesium alloys classification, while EN 1.8881 steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AZ61A magnesium and the bottom bar is EN 1.8881 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
190
Elongation at Break, % 11
16
Fatigue Strength, MPa 130
460
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 17
73
Shear Strength, MPa 150
510
Tensile Strength: Ultimate (UTS), MPa 280
830
Tensile Strength: Yield (Proof), MPa 170
710

Thermal Properties

Latent Heat of Fusion, J/g 350
260
Maximum Temperature: Mechanical, °C 120
420
Melting Completion (Liquidus), °C 600
1460
Melting Onset (Solidus), °C 530
1420
Specific Heat Capacity, J/kg-K 990
470
Thermal Conductivity, W/m-K 79
40
Thermal Expansion, µm/m-K 27
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 12
8.1
Electrical Conductivity: Equal Weight (Specific), % IACS 62
9.3

Otherwise Unclassified Properties

Base Metal Price, % relative 12
3.7
Density, g/cm3 1.7
7.8
Embodied Carbon, kg CO2/kg material 23
1.9
Embodied Energy, MJ/kg 160
26
Embodied Water, L/kg 980
54

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 27
120
Resilience: Unit (Modulus of Resilience), kJ/m3 310
1320
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 69
24
Strength to Weight: Axial, points 46
29
Strength to Weight: Bending, points 56
25
Thermal Diffusivity, mm2/s 47
11
Thermal Shock Resistance, points 17
24

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.5 to 7.2
0
Boron (B), % 0
0 to 0.0050
Carbon (C), % 0
0 to 0.2
Chromium (Cr), % 0
0 to 1.5
Copper (Cu), % 0 to 0.050
0 to 0.3
Iron (Fe), % 0 to 0.0050
91.9 to 100
Magnesium (Mg), % 90.3 to 93.9
0
Manganese (Mn), % 0.15 to 0.5
0 to 1.7
Molybdenum (Mo), % 0
0 to 0.7
Nickel (Ni), % 0 to 0.0050
0 to 2.5
Niobium (Nb), % 0
0 to 0.060
Nitrogen (N), % 0
0 to 0.015
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 0 to 0.1
0 to 0.8
Sulfur (S), % 0
0 to 0.0080
Titanium (Ti), % 0
0 to 0.050
Vanadium (V), % 0
0 to 0.12
Zinc (Zn), % 0.4 to 1.5
0
Zirconium (Zr), % 0
0 to 0.15
Residuals, % 0 to 0.3
0