AZ61A Magnesium vs. SAE-AISI 8660 Steel

AZ61A magnesium belongs to the magnesium alloys classification, while SAE-AISI 8660 steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AZ61A magnesium and the bottom bar is SAE-AISI 8660 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
190
Elongation at Break, % 11
12
Fatigue Strength, MPa 130
340
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 17
73
Shear Strength, MPa 150
390
Tensile Strength: Ultimate (UTS), MPa 280
660
Tensile Strength: Yield (Proof), MPa 170
550

Thermal Properties

Latent Heat of Fusion, J/g 350
250
Maximum Temperature: Mechanical, °C 120
410
Melting Completion (Liquidus), °C 600
1450
Melting Onset (Solidus), °C 530
1410
Specific Heat Capacity, J/kg-K 990
470
Thermal Conductivity, W/m-K 79
39
Thermal Expansion, µm/m-K 27
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 12
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 62
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 12
2.6
Density, g/cm3 1.7
7.8
Embodied Carbon, kg CO2/kg material 23
1.5
Embodied Energy, MJ/kg 160
20
Embodied Water, L/kg 980
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 27
73
Resilience: Unit (Modulus of Resilience), kJ/m3 310
800
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 69
24
Strength to Weight: Axial, points 46
23
Strength to Weight: Bending, points 56
21
Thermal Diffusivity, mm2/s 47
10
Thermal Shock Resistance, points 17
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.5 to 7.2
0
Carbon (C), % 0
0.56 to 0.64
Chromium (Cr), % 0
0.4 to 0.6
Copper (Cu), % 0 to 0.050
0
Iron (Fe), % 0 to 0.0050
96.4 to 97.6
Magnesium (Mg), % 90.3 to 93.9
0
Manganese (Mn), % 0.15 to 0.5
0.75 to 1.0
Molybdenum (Mo), % 0
0.15 to 0.25
Nickel (Ni), % 0 to 0.0050
0.4 to 0.7
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0 to 0.1
0.15 to 0.35
Sulfur (S), % 0
0 to 0.040
Zinc (Zn), % 0.4 to 1.5
0
Residuals, % 0 to 0.3
0