AZ61A Magnesium vs. SAE-AISI M3 Class 2 Steel

AZ61A magnesium belongs to the magnesium alloys classification, while SAE-AISI M3 class 2 steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AZ61A magnesium and the bottom bar is SAE-AISI M3 class 2 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 17
77
Tensile Strength: Ultimate (UTS), MPa 280
770 to 2210

Thermal Properties

Latent Heat of Fusion, J/g 350
260
Melting Completion (Liquidus), °C 600
1620
Melting Onset (Solidus), °C 530
1570
Specific Heat Capacity, J/kg-K 990
440
Thermal Conductivity, W/m-K 79
26
Thermal Expansion, µm/m-K 27
12

Otherwise Unclassified Properties

Base Metal Price, % relative 12
25
Density, g/cm3 1.7
8.3
Embodied Carbon, kg CO2/kg material 23
12
Embodied Energy, MJ/kg 160
180
Embodied Water, L/kg 980
110

Common Calculations

Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 69
23
Strength to Weight: Axial, points 46
26 to 74
Strength to Weight: Bending, points 56
22 to 45
Thermal Diffusivity, mm2/s 47
7.2
Thermal Shock Resistance, points 17
24 to 69

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.5 to 7.2
0
Carbon (C), % 0
1.2 to 1.3
Chromium (Cr), % 0
3.8 to 4.5
Copper (Cu), % 0 to 0.050
0 to 0.25
Iron (Fe), % 0 to 0.0050
75.8 to 82.3
Magnesium (Mg), % 90.3 to 93.9
0
Manganese (Mn), % 0.15 to 0.5
0.15 to 0.4
Molybdenum (Mo), % 0
4.8 to 6.5
Nickel (Ni), % 0 to 0.0050
0 to 0.3
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 0.1
0.2 to 0.45
Sulfur (S), % 0
0 to 0.030
Tungsten (W), % 0
5.0 to 6.8
Vanadium (V), % 0
2.8 to 3.8
Zinc (Zn), % 0.4 to 1.5
0
Residuals, % 0 to 0.3
0