AZ61A Magnesium vs. Titanium 15-3-3-3
AZ61A magnesium belongs to the magnesium alloys classification, while titanium 15-3-3-3 belongs to the titanium alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is AZ61A magnesium and the bottom bar is titanium 15-3-3-3.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 45 | |
| 100 |
| Elongation at Break, % | 11 | |
| 5.7 to 8.0 |
| Fatigue Strength, MPa | 130 | |
| 610 to 710 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 17 | |
| 39 |
| Shear Strength, MPa | 150 | |
| 660 to 810 |
| Tensile Strength: Ultimate (UTS), MPa | 280 | |
| 1120 to 1390 |
| Tensile Strength: Yield (Proof), MPa | 170 | |
| 1100 to 1340 |
Thermal Properties
| Latent Heat of Fusion, J/g | 350 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 430 |
| Melting Completion (Liquidus), °C | 600 | |
| 1620 |
| Melting Onset (Solidus), °C | 530 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 990 | |
| 520 |
| Thermal Conductivity, W/m-K | 79 | |
| 8.1 |
| Thermal Expansion, µm/m-K | 27 | |
| 9.8 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 12 | |
| 1.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 62 | |
| 2.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 40 |
| Density, g/cm3 | 1.7 | |
| 4.8 |
| Embodied Carbon, kg CO2/kg material | 23 | |
| 59 |
| Embodied Energy, MJ/kg | 160 | |
| 950 |
| Embodied Water, L/kg | 980 | |
| 260 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 27 | |
| 78 to 89 |
| Stiffness to Weight: Axial, points | 15 | |
| 12 |
| Stiffness to Weight: Bending, points | 69 | |
| 32 |
| Strength to Weight: Axial, points | 46 | |
| 64 to 80 |
| Strength to Weight: Bending, points | 56 | |
| 50 to 57 |
| Thermal Diffusivity, mm2/s | 47 | |
| 3.2 |
| Thermal Shock Resistance, points | 17 | |
| 79 to 98 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 5.5 to 7.2 | |
| 2.5 to 3.5 |
| Carbon (C), % | 0 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 | |
| 2.5 to 3.5 |
| Copper (Cu), % | 0 to 0.050 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 to 0.0050 | |
| 0 to 0.25 |
| Magnesium (Mg), % | 90.3 to 93.9 | |
| 0 |
| Manganese (Mn), % | 0.15 to 0.5 | |
| 0 |
| Nickel (Ni), % | 0 to 0.0050 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.050 |
| Oxygen (O), % | 0 | |
| 0 to 0.13 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 |
| Tin (Sn), % | 0 | |
| 2.5 to 3.5 |
| Titanium (Ti), % | 0 | |
| 72.6 to 78.5 |
| Vanadium (V), % | 0 | |
| 14 to 16 |
| Zinc (Zn), % | 0.4 to 1.5 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 to 0.4 |