AZ80A Magnesium vs. 5026 Aluminum
AZ80A magnesium belongs to the magnesium alloys classification, while 5026 aluminum belongs to the aluminum alloys.
For each property being compared, the top bar is AZ80A magnesium and the bottom bar is 5026 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 46 | |
| 70 |
| Elongation at Break, % | 3.9 to 8.5 | |
| 5.1 to 11 |
| Fatigue Strength, MPa | 140 to 170 | |
| 94 to 140 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 18 | |
| 26 |
| Shear Strength, MPa | 160 to 190 | |
| 150 to 180 |
| Tensile Strength: Ultimate (UTS), MPa | 320 to 340 | |
| 260 to 320 |
| Tensile Strength: Yield (Proof), MPa | 210 to 230 | |
| 120 to 250 |
Thermal Properties
| Latent Heat of Fusion, J/g | 350 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 130 | |
| 210 |
| Melting Completion (Liquidus), °C | 600 | |
| 650 |
| Melting Onset (Solidus), °C | 490 | |
| 510 |
| Specific Heat Capacity, J/kg-K | 990 | |
| 890 |
| Thermal Conductivity, W/m-K | 77 | |
| 130 |
| Thermal Expansion, µm/m-K | 26 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 11 | |
| 31 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 59 | |
| 99 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 9.5 |
| Density, g/cm3 | 1.7 | |
| 2.8 |
| Embodied Carbon, kg CO2/kg material | 23 | |
| 8.9 |
| Embodied Energy, MJ/kg | 160 | |
| 150 |
| Embodied Water, L/kg | 990 | |
| 1150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 24 | |
| 15 to 29 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 500 to 600 | |
| 100 to 440 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 69 | |
| 49 |
| Strength to Weight: Axial, points | 51 to 55 | |
| 26 to 32 |
| Strength to Weight: Bending, points | 60 to 63 | |
| 33 to 37 |
| Thermal Diffusivity, mm2/s | 45 | |
| 52 |
| Thermal Shock Resistance, points | 19 to 20 | |
| 11 to 14 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 7.8 to 9.2 | |
| 88.2 to 94.7 |
| Chromium (Cr), % | 0 | |
| 0 to 0.3 |
| Copper (Cu), % | 0 to 0.050 | |
| 0.1 to 0.8 |
| Iron (Fe), % | 0 to 0.0050 | |
| 0.2 to 1.0 |
| Magnesium (Mg), % | 89 to 91.9 | |
| 3.9 to 4.9 |
| Manganese (Mn), % | 0.12 to 0.5 | |
| 0.6 to 1.8 |
| Nickel (Ni), % | 0 to 0.0050 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 0.55 to 1.4 |
| Titanium (Ti), % | 0 | |
| 0 to 0.2 |
| Zinc (Zn), % | 0.2 to 0.8 | |
| 0 to 1.0 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.3 |
| Residuals, % | 0 to 0.3 | |
| 0 to 0.15 |