AZ81A Magnesium vs. C85200 Brass

AZ81A magnesium belongs to the magnesium alloys classification, while C85200 brass belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AZ81A magnesium and the bottom bar is C85200 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 46
110
Elongation at Break, % 3.0 to 8.8
28
Poisson's Ratio 0.29
0.32
Shear Modulus, GPa 18
40
Tensile Strength: Ultimate (UTS), MPa 160 to 240
270
Tensile Strength: Yield (Proof), MPa 84
95

Thermal Properties

Latent Heat of Fusion, J/g 350
180
Maximum Temperature: Mechanical, °C 130
140
Melting Completion (Liquidus), °C 600
940
Melting Onset (Solidus), °C 500
930
Specific Heat Capacity, J/kg-K 990
380
Thermal Conductivity, W/m-K 84
84
Thermal Expansion, µm/m-K 27
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 12
18
Electrical Conductivity: Equal Weight (Specific), % IACS 65
19

Otherwise Unclassified Properties

Base Metal Price, % relative 12
26
Density, g/cm3 1.7
8.4
Embodied Carbon, kg CO2/kg material 23
2.8
Embodied Energy, MJ/kg 160
46
Embodied Water, L/kg 990
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 4.0 to 17
59
Resilience: Unit (Modulus of Resilience), kJ/m3 77 to 78
42
Stiffness to Weight: Axial, points 15
7.0
Stiffness to Weight: Bending, points 70
19
Strength to Weight: Axial, points 26 to 39
8.9
Strength to Weight: Bending, points 38 to 50
11
Thermal Diffusivity, mm2/s 50
27
Thermal Shock Resistance, points 9.1 to 14
9.3

Alloy Composition

Aluminum (Al), % 7.0 to 8.1
0 to 0.0050
Antimony (Sb), % 0
0 to 0.2
Copper (Cu), % 0 to 0.1
70 to 74
Iron (Fe), % 0
0 to 0.6
Lead (Pb), % 0
1.5 to 3.8
Magnesium (Mg), % 89.8 to 92.5
0
Manganese (Mn), % 0.13 to 0.35
0
Nickel (Ni), % 0 to 0.010
0 to 1.0
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 0 to 0.3
0 to 0.050
Sulfur (S), % 0
0 to 0.050
Tin (Sn), % 0
0.7 to 2.0
Zinc (Zn), % 0.4 to 1.0
20 to 27
Residuals, % 0 to 0.3
0 to 0.9