AZ81A Magnesium vs. C94300 Bronze

AZ81A magnesium belongs to the magnesium alloys classification, while C94300 bronze belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AZ81A magnesium and the bottom bar is C94300 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 46
87
Elongation at Break, % 3.0 to 8.8
9.7
Poisson's Ratio 0.29
0.36
Shear Modulus, GPa 18
32
Tensile Strength: Ultimate (UTS), MPa 160 to 240
180
Tensile Strength: Yield (Proof), MPa 84
120

Thermal Properties

Latent Heat of Fusion, J/g 350
150
Maximum Temperature: Mechanical, °C 130
110
Melting Completion (Liquidus), °C 600
820
Melting Onset (Solidus), °C 500
760
Specific Heat Capacity, J/kg-K 990
320
Thermal Conductivity, W/m-K 84
63
Thermal Expansion, µm/m-K 27
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 12
9.0
Electrical Conductivity: Equal Weight (Specific), % IACS 65
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 12
28
Density, g/cm3 1.7
9.3
Embodied Carbon, kg CO2/kg material 23
2.9
Embodied Energy, MJ/kg 160
47
Embodied Water, L/kg 990
370

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 4.0 to 17
15
Resilience: Unit (Modulus of Resilience), kJ/m3 77 to 78
77
Stiffness to Weight: Axial, points 15
5.2
Stiffness to Weight: Bending, points 70
16
Strength to Weight: Axial, points 26 to 39
5.2
Strength to Weight: Bending, points 38 to 50
7.4
Thermal Diffusivity, mm2/s 50
21
Thermal Shock Resistance, points 9.1 to 14
7.1

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 7.0 to 8.1
0 to 0.0050
Antimony (Sb), % 0
0 to 0.8
Copper (Cu), % 0 to 0.1
67 to 72
Iron (Fe), % 0
0 to 0.15
Lead (Pb), % 0
23 to 27
Magnesium (Mg), % 89.8 to 92.5
0
Manganese (Mn), % 0.13 to 0.35
0
Nickel (Ni), % 0 to 0.010
0 to 1.0
Phosphorus (P), % 0
0 to 1.5
Silicon (Si), % 0 to 0.3
0 to 0.0050
Sulfur (S), % 0
0 to 0.080
Tin (Sn), % 0
4.5 to 6.0
Zinc (Zn), % 0.4 to 1.0
0 to 0.8
Residuals, % 0 to 0.3
0 to 1.0