AZ81A Magnesium vs. S30615 Stainless Steel
AZ81A magnesium belongs to the magnesium alloys classification, while S30615 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is AZ81A magnesium and the bottom bar is S30615 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 55 | |
| 190 |
| Elastic (Young's, Tensile) Modulus, GPa | 46 | |
| 190 |
| Elongation at Break, % | 3.0 to 8.8 | |
| 39 |
| Fatigue Strength, MPa | 78 to 80 | |
| 270 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 18 | |
| 75 |
| Shear Strength, MPa | 91 to 130 | |
| 470 |
| Tensile Strength: Ultimate (UTS), MPa | 160 to 240 | |
| 690 |
| Tensile Strength: Yield (Proof), MPa | 84 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 350 | |
| 340 |
| Maximum Temperature: Mechanical, °C | 130 | |
| 960 |
| Melting Completion (Liquidus), °C | 600 | |
| 1370 |
| Melting Onset (Solidus), °C | 500 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 990 | |
| 500 |
| Thermal Conductivity, W/m-K | 84 | |
| 14 |
| Thermal Expansion, µm/m-K | 27 | |
| 16 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 19 |
| Density, g/cm3 | 1.7 | |
| 7.6 |
| Embodied Carbon, kg CO2/kg material | 23 | |
| 3.7 |
| Embodied Energy, MJ/kg | 160 | |
| 53 |
| Embodied Water, L/kg | 990 | |
| 170 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.0 to 17 | |
| 220 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 77 to 78 | |
| 260 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 70 | |
| 25 |
| Strength to Weight: Axial, points | 26 to 39 | |
| 25 |
| Strength to Weight: Bending, points | 38 to 50 | |
| 23 |
| Thermal Diffusivity, mm2/s | 50 | |
| 3.7 |
| Thermal Shock Resistance, points | 9.1 to 14 | |
| 16 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 7.0 to 8.1 | |
| 0.8 to 1.5 |
| Carbon (C), % | 0 | |
| 0.16 to 0.24 |
| Chromium (Cr), % | 0 | |
| 17 to 19.5 |
| Copper (Cu), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 | |
| 56.7 to 65.3 |
| Magnesium (Mg), % | 89.8 to 92.5 | |
| 0 |
| Manganese (Mn), % | 0.13 to 0.35 | |
| 0 to 2.0 |
| Nickel (Ni), % | 0 to 0.010 | |
| 13.5 to 16 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.3 | |
| 3.2 to 4.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Zinc (Zn), % | 0.4 to 1.0 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 |