AZ91A Magnesium vs. ACI-ASTM CH20 Steel

AZ91A magnesium belongs to the magnesium alloys classification, while ACI-ASTM CH20 steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AZ91A magnesium and the bottom bar is ACI-ASTM CH20 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 63
190
Elastic (Young's, Tensile) Modulus, GPa 46
200
Elongation at Break, % 5.0
38
Fatigue Strength, MPa 99
290
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 18
78
Tensile Strength: Ultimate (UTS), MPa 240
610
Tensile Strength: Yield (Proof), MPa 160
350

Thermal Properties

Latent Heat of Fusion, J/g 360
310
Maximum Temperature: Mechanical, °C 130
1100
Melting Completion (Liquidus), °C 600
1410
Melting Onset (Solidus), °C 470
1430
Specific Heat Capacity, J/kg-K 990
480
Thermal Conductivity, W/m-K 73
14
Thermal Expansion, µm/m-K 26
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 10
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 52
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 12
20
Density, g/cm3 1.7
7.8
Embodied Carbon, kg CO2/kg material 22
3.7
Embodied Energy, MJ/kg 160
53
Embodied Water, L/kg 990
180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 11
200
Resilience: Unit (Modulus of Resilience), kJ/m3 280
300
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 69
25
Strength to Weight: Axial, points 38
22
Strength to Weight: Bending, points 49
21
Thermal Diffusivity, mm2/s 42
3.7
Thermal Shock Resistance, points 14
15

Alloy Composition

Aluminum (Al), % 8.3 to 9.7
0
Carbon (C), % 0
0 to 0.2
Chromium (Cr), % 0
22 to 26
Copper (Cu), % 0 to 0.1
0
Iron (Fe), % 0
54.7 to 66
Magnesium (Mg), % 88.2 to 91.2
0
Manganese (Mn), % 0.13 to 0.5
0 to 1.5
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0 to 0.030
12 to 15
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 2.0
Sulfur (S), % 0
0 to 0.040
Zinc (Zn), % 0.35 to 1.0
0