AZ91A Magnesium vs. ASTM A369 Grade FP91

AZ91A magnesium belongs to the magnesium alloys classification, while ASTM A369 grade FP91 belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AZ91A magnesium and the bottom bar is ASTM A369 grade FP91.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 63
200
Elastic (Young's, Tensile) Modulus, GPa 46
190
Elongation at Break, % 5.0
19
Fatigue Strength, MPa 99
320
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 18
75
Shear Strength, MPa 140
410
Tensile Strength: Ultimate (UTS), MPa 240
670
Tensile Strength: Yield (Proof), MPa 160
460

Thermal Properties

Latent Heat of Fusion, J/g 360
270
Maximum Temperature: Mechanical, °C 130
600
Melting Completion (Liquidus), °C 600
1460
Melting Onset (Solidus), °C 470
1420
Specific Heat Capacity, J/kg-K 990
470
Thermal Conductivity, W/m-K 73
26
Thermal Expansion, µm/m-K 26
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 10
8.9
Electrical Conductivity: Equal Weight (Specific), % IACS 52
10

Otherwise Unclassified Properties

Base Metal Price, % relative 12
7.0
Density, g/cm3 1.7
7.8
Embodied Carbon, kg CO2/kg material 22
2.6
Embodied Energy, MJ/kg 160
37
Embodied Water, L/kg 990
88

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 11
110
Resilience: Unit (Modulus of Resilience), kJ/m3 280
560
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 69
25
Strength to Weight: Axial, points 38
24
Strength to Weight: Bending, points 49
22
Thermal Diffusivity, mm2/s 42
6.9
Thermal Shock Resistance, points 14
18

Alloy Composition

Aluminum (Al), % 8.3 to 9.7
0 to 0.020
Carbon (C), % 0
0.080 to 0.12
Chromium (Cr), % 0
8.0 to 9.5
Copper (Cu), % 0 to 0.1
0
Iron (Fe), % 0
87.3 to 90.3
Magnesium (Mg), % 88.2 to 91.2
0
Manganese (Mn), % 0.13 to 0.5
0.3 to 0.6
Molybdenum (Mo), % 0
0.85 to 1.1
Nickel (Ni), % 0 to 0.030
0 to 0.4
Niobium (Nb), % 0
0.060 to 0.1
Nitrogen (N), % 0
0.030 to 0.070
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 0.5
0.2 to 0.5
Sulfur (S), % 0
0 to 0.025
Titanium (Ti), % 0
0 to 0.010
Vanadium (V), % 0
0.18 to 0.25
Zinc (Zn), % 0.35 to 1.0
0
Zirconium (Zr), % 0
0 to 0.010