AZ91A Magnesium vs. Grade TDCrV Steel

AZ91A magnesium belongs to the magnesium alloys classification, while grade TDCrV steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AZ91A magnesium and the bottom bar is grade TDCrV steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 63
520
Elastic (Young's, Tensile) Modulus, GPa 46
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 18
80
Tensile Strength: Ultimate (UTS), MPa 240
1730

Thermal Properties

Latent Heat of Fusion, J/g 360
250
Maximum Temperature: Mechanical, °C 130
410
Melting Completion (Liquidus), °C 600
1450
Melting Onset (Solidus), °C 470
1410
Specific Heat Capacity, J/kg-K 990
470
Thermal Conductivity, W/m-K 73
49
Thermal Expansion, µm/m-K 26
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 10
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 52
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 12
2.1
Density, g/cm3 1.7
7.8
Embodied Carbon, kg CO2/kg material 22
1.9
Embodied Energy, MJ/kg 160
26
Embodied Water, L/kg 990
49

Common Calculations

Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 69
24
Strength to Weight: Axial, points 38
61
Strength to Weight: Bending, points 49
41
Thermal Diffusivity, mm2/s 42
13
Thermal Shock Resistance, points 14
51

Alloy Composition

Aluminum (Al), % 8.3 to 9.7
0
Carbon (C), % 0
0.62 to 0.72
Chromium (Cr), % 0
0.4 to 0.6
Copper (Cu), % 0 to 0.1
0 to 0.1
Iron (Fe), % 0
97.8 to 98.8
Magnesium (Mg), % 88.2 to 91.2
0
Manganese (Mn), % 0.13 to 0.5
0.5 to 0.9
Nickel (Ni), % 0 to 0.030
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 0.5
0.15 to 0.3
Sulfur (S), % 0
0 to 0.020
Vanadium (V), % 0
0.15 to 0.25
Zinc (Zn), % 0.35 to 1.0
0