MakeItFrom.com
Menu (ESC)

AZ91A Magnesium vs. Solder Alloy 114

AZ91A magnesium belongs to the magnesium alloys classification, while solder alloy 114 belongs to the otherwise unclassified metals. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AZ91A magnesium and the bottom bar is solder alloy 114.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 63
12
Elastic (Young's, Tensile) Modulus, GPa 46
30
Elongation at Break, % 5.0
25
Poisson's Ratio 0.29
0.41
Shear Modulus, GPa 18
11
Tensile Strength: Ultimate (UTS), MPa 240
37

Thermal Properties

Latent Heat of Fusion, J/g 360
38
Melting Completion (Liquidus), °C 600
240
Melting Onset (Solidus), °C 470
180
Specific Heat Capacity, J/kg-K 990
170
Thermal Conductivity, W/m-K 73
44
Thermal Expansion, µm/m-K 26
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 10
10
Electrical Conductivity: Equal Weight (Specific), % IACS 52
9.4

Otherwise Unclassified Properties

Base Metal Price, % relative 12
95
Density, g/cm3 1.7
9.7
Embodied Carbon, kg CO2/kg material 22
8.3
Embodied Energy, MJ/kg 160
140
Embodied Water, L/kg 990
760

Common Calculations

Stiffness to Weight: Axial, points 15
1.7
Stiffness to Weight: Bending, points 69
11
Strength to Weight: Axial, points 38
1.1
Strength to Weight: Bending, points 49
2.6
Thermal Diffusivity, mm2/s 42
27
Thermal Shock Resistance, points 14
3.4

Alloy Composition

Aluminum (Al), % 8.3 to 9.7
0 to 0.0010
Antimony (Sb), % 0
0 to 0.5
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.25
Cadmium (Cd), % 0
0 to 0.0050
Copper (Cu), % 0 to 0.1
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0
0 to 0.020
Lead (Pb), % 0
58.4 to 60.5
Magnesium (Mg), % 88.2 to 91.2
0
Manganese (Mn), % 0.13 to 0.5
0
Nickel (Ni), % 0 to 0.030
0 to 0.010
Silicon (Si), % 0 to 0.5
0
Silver (Ag), % 0
0 to 0.1
Tin (Sn), % 0
39.5 to 40.5
Zinc (Zn), % 0.35 to 1.0
0 to 0.0010