AZ91B Magnesium vs. AISI 304Cu Stainless Steel

AZ91B magnesium belongs to the magnesium alloys classification, while AISI 304Cu stainless steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AZ91B magnesium and the bottom bar is AISI 304Cu stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 63
160
Elastic (Young's, Tensile) Modulus, GPa 46
190
Elongation at Break, % 5.0
45
Fatigue Strength, MPa 79
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 18
76
Shear Strength, MPa 140
370
Tensile Strength: Ultimate (UTS), MPa 240
530
Tensile Strength: Yield (Proof), MPa 160
210

Thermal Properties

Latent Heat of Fusion, J/g 360
290
Maximum Temperature: Mechanical, °C 130
930
Melting Completion (Liquidus), °C 600
1410
Melting Onset (Solidus), °C 470
1370
Specific Heat Capacity, J/kg-K 990
480
Thermal Conductivity, W/m-K 73
13
Thermal Expansion, µm/m-K 26
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 58
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 12
16
Density, g/cm3 1.7
7.8
Embodied Carbon, kg CO2/kg material 22
3.0
Embodied Energy, MJ/kg 160
43
Embodied Water, L/kg 990
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 11
190
Resilience: Unit (Modulus of Resilience), kJ/m3 280
110
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 69
25
Strength to Weight: Axial, points 38
19
Strength to Weight: Bending, points 49
19
Thermal Diffusivity, mm2/s 42
3.5
Thermal Shock Resistance, points 14
12

Alloy Composition

Aluminum (Al), % 8.3 to 9.7
0
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
17 to 19
Copper (Cu), % 0 to 0.35
3.0 to 4.0
Iron (Fe), % 0
63.9 to 72
Magnesium (Mg), % 87.9 to 91.2
0
Manganese (Mn), % 0.13 to 0.5
0 to 2.0
Nickel (Ni), % 0 to 0.030
8.0 to 10
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Zinc (Zn), % 0.35 to 1.0
0