AZ91B Magnesium vs. EN 1.3975 Stainless Steel

AZ91B magnesium belongs to the magnesium alloys classification, while EN 1.3975 stainless steel belongs to the iron alloys. There are 26 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AZ91B magnesium and the bottom bar is EN 1.3975 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 63
190
Elastic (Young's, Tensile) Modulus, GPa 46
190
Elongation at Break, % 5.0
27
Fatigue Strength, MPa 79
230
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 18
76
Tensile Strength: Ultimate (UTS), MPa 240
660
Tensile Strength: Yield (Proof), MPa 160
320

Thermal Properties

Latent Heat of Fusion, J/g 360
340
Maximum Temperature: Mechanical, °C 130
910
Melting Completion (Liquidus), °C 600
1360
Melting Onset (Solidus), °C 470
1320
Specific Heat Capacity, J/kg-K 990
500
Thermal Expansion, µm/m-K 26
16

Otherwise Unclassified Properties

Base Metal Price, % relative 12
15
Density, g/cm3 1.7
7.5
Embodied Carbon, kg CO2/kg material 22
3.3
Embodied Energy, MJ/kg 160
47
Embodied Water, L/kg 990
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 11
150
Resilience: Unit (Modulus of Resilience), kJ/m3 280
270
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 69
26
Strength to Weight: Axial, points 38
24
Strength to Weight: Bending, points 49
22
Thermal Shock Resistance, points 14
15

Alloy Composition

Aluminum (Al), % 8.3 to 9.7
0
Carbon (C), % 0
0 to 0.050
Chromium (Cr), % 0
16 to 18
Copper (Cu), % 0 to 0.35
0
Iron (Fe), % 0
58.2 to 65.4
Magnesium (Mg), % 87.9 to 91.2
0
Manganese (Mn), % 0.13 to 0.5
7.0 to 9.0
Molybdenum (Mo), % 0
0 to 1.0
Nickel (Ni), % 0 to 0.030
8.0 to 9.0
Nitrogen (N), % 0
0.080 to 0.18
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0 to 0.5
3.5 to 4.5
Sulfur (S), % 0
0 to 0.030
Zinc (Zn), % 0.35 to 1.0
0