AZ91B Magnesium vs. N08700 Stainless Steel

AZ91B magnesium belongs to the magnesium alloys classification, while N08700 stainless steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AZ91B magnesium and the bottom bar is N08700 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 63
170
Elastic (Young's, Tensile) Modulus, GPa 46
200
Elongation at Break, % 5.0
32
Fatigue Strength, MPa 79
210
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 18
79
Shear Strength, MPa 140
410
Tensile Strength: Ultimate (UTS), MPa 240
620
Tensile Strength: Yield (Proof), MPa 160
270

Thermal Properties

Latent Heat of Fusion, J/g 360
300
Maximum Temperature: Mechanical, °C 130
1100
Melting Completion (Liquidus), °C 600
1450
Melting Onset (Solidus), °C 470
1400
Specific Heat Capacity, J/kg-K 990
470
Thermal Conductivity, W/m-K 73
13
Thermal Expansion, µm/m-K 26
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 58
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 12
32
Density, g/cm3 1.7
8.1
Embodied Carbon, kg CO2/kg material 22
6.0
Embodied Energy, MJ/kg 160
82
Embodied Water, L/kg 990
200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 11
160
Resilience: Unit (Modulus of Resilience), kJ/m3 280
180
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 69
24
Strength to Weight: Axial, points 38
21
Strength to Weight: Bending, points 49
20
Thermal Diffusivity, mm2/s 42
3.5
Thermal Shock Resistance, points 14
14

Alloy Composition

Aluminum (Al), % 8.3 to 9.7
0
Carbon (C), % 0
0 to 0.040
Chromium (Cr), % 0
19 to 23
Copper (Cu), % 0 to 0.35
0 to 0.5
Iron (Fe), % 0
42 to 52.7
Magnesium (Mg), % 87.9 to 91.2
0
Manganese (Mn), % 0.13 to 0.5
0 to 2.0
Molybdenum (Mo), % 0
4.3 to 5.0
Nickel (Ni), % 0 to 0.030
24 to 26
Niobium (Nb), % 0
0 to 0.4
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Zinc (Zn), % 0.35 to 1.0
0