AZ91D Magnesium vs. 90-silver 10-tin-oxide
AZ91D magnesium belongs to the magnesium alloys classification, while 90-silver 10-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (28, in this case) are not shown.
For each property being compared, the top bar is AZ91D magnesium and the bottom bar is 90-silver 10-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 11 | |
| 77 to 82 |
| Elongation at Break, % | 2.3 to 4.5 | |
| 7.0 to 35 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.2 to 7.7 | |
| 20 to 68 |
| Shear Strength, MPa | 120 to 140 | |
| 160 to 170 |
| Tensile Strength: Ultimate (UTS), MPa | 160 to 220 | |
| 230 to 300 |
| Tensile Strength: Yield (Proof), MPa | 80 to 130 | |
| 120 to 280 |