AZ91E Magnesium vs. AISI 303 Stainless Steel
AZ91E magnesium belongs to the magnesium alloys classification, while AISI 303 stainless steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is AZ91E magnesium and the bottom bar is AISI 303 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 75 | |
| 170 to 210 |
| Elastic (Young's, Tensile) Modulus, GPa | 46 | |
| 200 |
| Elongation at Break, % | 2.5 to 6.2 | |
| 40 to 51 |
| Fatigue Strength, MPa | 81 to 85 | |
| 230 to 360 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 18 | |
| 77 |
| Shear Strength, MPa | 89 to 150 | |
| 430 to 470 |
| Tensile Strength: Ultimate (UTS), MPa | 160 to 260 | |
| 600 to 690 |
| Tensile Strength: Yield (Proof), MPa | 96 to 130 | |
| 230 to 420 |
Thermal Properties
| Latent Heat of Fusion, J/g | 350 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 130 | |
| 930 |
| Melting Completion (Liquidus), °C | 600 | |
| 1450 |
| Melting Onset (Solidus), °C | 500 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 990 | |
| 480 |
| Thermal Conductivity, W/m-K | 84 | |
| 16 |
| Thermal Expansion, µm/m-K | 27 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 10 to 12 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 52 to 60 | |
| 2.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 15 |
| Density, g/cm3 | 1.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 22 | |
| 3.0 |
| Embodied Energy, MJ/kg | 160 | |
| 42 |
| Embodied Water, L/kg | 990 | |
| 140 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 3.4 to 12 | |
| 240 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 100 to 190 | |
| 140 to 440 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 69 | |
| 25 |
| Strength to Weight: Axial, points | 25 to 42 | |
| 21 to 25 |
| Strength to Weight: Bending, points | 37 to 53 | |
| 20 to 22 |
| Thermal Diffusivity, mm2/s | 49 | |
| 4.4 |
| Thermal Shock Resistance, points | 9.0 to 15 | |
| 13 to 15 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 8.1 to 9.3 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.15 |
| Chromium (Cr), % | 0 | |
| 17 to 19 |
| Copper (Cu), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.0050 | |
| 67.3 to 74.9 |
| Magnesium (Mg), % | 88.8 to 91.3 | |
| 0 |
| Manganese (Mn), % | 0.17 to 0.35 | |
| 0 to 2.0 |
| Nickel (Ni), % | 0 to 0.0010 | |
| 8.0 to 10 |
| Phosphorus (P), % | 0 | |
| 0 to 0.2 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0.15 to 0.35 |
| Zinc (Zn), % | 0.4 to 1.0 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 |