NBR Rubber vs. PAI
NBR rubber belongs to the thermoset elastomers (rubber) classification, while PAI belongs to the thermoplastics. There are 10 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is NBR rubber and the bottom bar is PAI.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.3 | |
| 1.4 to 1.6 |
| Elongation at Break, % | 380 | |
| 3.0 to 12 |
| Glass Transition Temperature, °C | -30 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 110 | |
| 260 |
| Specific Heat Capacity, J/kg-K | 1350 | |
| 910 to 1000 |
| Strength to Weight: Axial, points | 3.9 | |
| 19 to 34 |
| Strength to Weight: Bending, points | 12 | |
| 33 to 49 |
| Tensile Strength: Ultimate (UTS), MPa | 18 | |
| 100 to 180 |
| Thermal Conductivity, W/m-K | 0.25 | |
| 0.26 to 0.53 |
| Thermal Diffusivity, mm2/s | 0.15 | |
| 0.16 to 0.41 |