Age Hardened ASTM B563 vs. Aged Titanium 4-4-2
Age hardened ASTM B563 belongs to the otherwise unclassified metals classification, while aged titanium 4-4-2 belongs to the titanium alloys. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is age hardened ASTM B563 and the bottom bar is aged titanium 4-4-2.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 110 |
| Elongation at Break, % | 7.0 | |
| 10 |
| Fatigue Strength, MPa | 310 | |
| 620 |
| Poisson's Ratio | 0.37 | |
| 0.32 |
| Shear Modulus, GPa | 37 | |
| 42 |
| Shear Strength, MPa | 690 | |
| 750 |
| Tensile Strength: Ultimate (UTS), MPa | 1170 | |
| 1250 |
Thermal Properties
| Latent Heat of Fusion, J/g | 150 | |
| 410 |
| Melting Completion (Liquidus), °C | 1180 | |
| 1610 |
| Melting Onset (Solidus), °C | 1030 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 260 | |
| 540 |
| Thermal Expansion, µm/m-K | 14 | |
| 8.6 |
Otherwise Unclassified Properties
| Density, g/cm3 | 11 | |
| 4.7 |
Common Calculations
| Stiffness to Weight: Axial, points | 5.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 14 | |
| 34 |
| Strength to Weight: Axial, points | 30 | |
| 74 |
| Strength to Weight: Bending, points | 22 | |
| 55 |
| Thermal Shock Resistance, points | 61 | |
| 93 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 3.0 to 5.0 |
| Carbon (C), % | 0 | |
| 0 to 0.080 |
| Copper (Cu), % | 15.5 to 16.5 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 | |
| 0 to 0.2 |
| Molybdenum (Mo), % | 0 | |
| 3.0 to 5.0 |
| Nickel (Ni), % | 0.8 to 1.2 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.050 |
| Oxygen (O), % | 0 | |
| 0 to 0.25 |
| Palladium (Pd), % | 43 to 45 | |
| 0 |
| Platinum (Pt), % | 0.8 to 1.2 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0.3 to 0.7 |
| Silver (Ag), % | 37 to 39 | |
| 0 |
| Tin (Sn), % | 0 | |
| 1.5 to 2.5 |
| Titanium (Ti), % | 0 | |
| 85.8 to 92.2 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.4 |