Alumina-lime-silica Glass vs. C-310 Titania-based Ceramic

Alumina-lime-silica glass belongs to the glass and glass-ceramics classification, while C-310 titania-based ceramic belongs to the oxide-based engineering ceramics. There are 8 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is alumina-lime-silica glass and the bottom bar is C-310 titania-based ceramic.

Metric UnitsUS Customary Units

Material Properties

Density, g/cm3 2.8
3.7
Dielectric Constant (Relative Permittivity) At 1 Hz 6.5
70
Dielectric Strength (Breakdown Potential), kV/mm 34
9.0
Electrical Dissipation At 1 Hz 0.0022
0.0056
Electrical Dissipation At 1 MHz 0.0026
0.0018
Electrical Resistivity Order of Magnitude, 10x Ω-m 12
10
Flexural Strength, MPa 46
75
Thermal Expansion, µm/m-K 4.3
7.0